Effect of Bonding Agents on the Shear Bond Strength of Tooth-colored Restorative Materials to Dentin: An In Vitro Study.

AIM: The aim of the study is to determine the difference in the shear bond strengths to dentin among dental composite (Filtek Z350®, 3M), compomer (Dyract Flow®, Dentsply) and Giomer (Beautifil®, Shofu) with 3MTM Single BondTM Universal Adhesive (SBU) (7th generation, self-etch, single solution adhesive) and AdperTM Single Bond 2 Adhesive (ASB) (5th generation, total-etch, two solution adhesive). MATERIALS AND METHODS: Sixty extracted human permanent teeth were collected, cleansed of debris, and placed in distilled water. The samples were segregated into two groups depicting the two bonding agents-AdperTM (ASB) and 3MTM Single Bond Universal (SBU) and sub-grouped into three groups depicting the three restorative materials (Composite, Giomer, and Compomer) used. Groups were respresented as follows: Group I-ASB + Composite; Group II-ASB + Giomer; Group III-ASB + Compomer; Group IV-SBU + Giomer; Group V-SBU + Compomer; Group VI-SBU + Composite. After applying the bonding agent as per the manufacturer's instructions, following which the restorative material was placed. A Universal Testing Machine (Instron 3366, UK) was employed to estimate the shear bond strength of the individual restorative material and shear bond strengths were calculated. RESULTS: Composite bonded with SBU (group VI) displayed the greatest shear strength (11.16 ± 4.22 MPa). Moreover, Giomers and flowable compomers displayed better bond strengths with ASB compared with their SBU-bonded counterparts. CONCLUSION: These results mark the importance of careful material selection in clinical practice and the bonding agent used to achieve optimal bond strength and enhance the clinical longevity and durability of dental restorations. CLINICAL SIGNIFICANCE: From a clinical perspective, to avoid a compressive or a shear failure, it would be preferrable to use a direct composite restorative material with SBU (Single bond universal adhesive, 7th generation) to achieve maximum bond strength. How to cite this article: Kuchibhotla N, Sathyamoorthy H, Balakrishnan S, et al. Effect of Bonding Agents on the Shear Bond Strength of Tooth-colored Restorative Materials to Dentin: An In Vitro Study. J Contemp Dent Pract 2024;25(3):245-249.

Cytotoxic effect of dental luting cement on human gingival mesenchymal stem cell and evaluation of cytokines and growth factor release - An in vitro study.

AIM: In routine dental care, various dental luting cements are utilized to cement the dental prosthesis. Thus, the aim of the current study was to assess the Cytotoxic effect of three different dental luting cements on human gingival mesenchymal stem cell and evaluation of cytokines and growth factors release. SETTINGS AND DESIGN: Cytotoxicity of glass ionomer cement (GIC), resin modified glass ionomer cement (RMGIC) and resin cement (RC) on the human gingival mesenchymal stem cells (HGMSCs) was evaluated. Amongst the cements tested, least cytotoxic cement was further tested for the release of cytokines and growth factors. MATERIALS AND METHODS: MTT test was used to evaluate the cytotoxicity of the dental luting cements at 1 h, 24 h, and 48 h on HGMSCs. Cytokines such as interleukin (IL) 1α & IL 8 and growth factors such as platelet derived growth factor & transforming growth factor beta release from the least cytotoxic RC was evaluated using flow cytometry analysis. STATISTICAL ANALYSIS USED: The mean absorbance values by MTT assay and cell viability at various time intervals between four groups were compared using a one way analysis of variance test and Tukey's post hoc test. The least cytotoxic RC group and the control group's mean levels of cytokines and growth factors were compared using the Mann-Whitney test. RESULT: As exposure time increased, the dental luting cement examined in this study were cytotoxic. RC was the least cytotoxic, RMGIC was moderate and glass ionomer cement showed the highest cytotoxic effect. Concomitantly, a significant positive biological response of gingival mesenchymal stem cells with the release of ILs when exposed to the RC was observed. CONCLUSION: For a fixed dental prosthesis to be clinically successful over the long term, it is imperative that the biocompatibility of the luting cement be taken into account in order to maintain a healthy periodontium surrounding the restoration.

Effect of various surface coating methods on surface roughness, micromorphological analysis and fluoride release from contemporary glass ionomer restorations.

OBJECTIVE: To evaluate the effect of various surface coating methods on surface roughness, micromorphological analysis and fluoride release from contemporary resin-modified and conventional glass ionomer restorations. MATERIALS & METHODS: A total of 72 permanent human molars were used in this study. The teeth were randomly assigned into 2 groups according to type of restorative materials used; resin modified glass ionomer cement and conventional glass ionomer (SDI Limited. Bayswater Victoria, Australia). Each group was subdivided into 3 subgroups according to the application of coat material; Sub-group1: without application of coat; Sub-group2: manufacturer recommended coat was applied and sub-group3: customized (vaseline) coat was applied. Each group was then subdivided into two divisions according to the time of testing; immediate (after 24 h) and delayed (after 6 months of storage). Three specimens from each sub-group were selected for surface roughness test (AFM) and another 3 specimens for the micromorphological analysis using scanning electron microscope (SEM). For the fluoride release test, a total of 60 cylindrical discs were used (n = 60). The discs were randomly split into 2 groups according to type of restorative materials used (n = 30); resin modified glass ionomer cement and conventional glass ionomer. Each group was subdivided into 3 subgroups (n = 10) according to the application of the coat material; Sub-group1: without application of coat; Sub-group2: with the manufacturer recommended coat and sub-group3: with application of customized (vaseline) coat. Data for each test was then collected, tabulated, were collected, tabulated, and tested for the normality with Shapiro-Wilk test. Based on the outcome of normality test, the significant effects of variables were assessed using appropriate statistical analysis testing methods. RESULTS: Regarding the data obtained from surface roughness test, Shapiro-Wilk test showed normal distribution pattern of all values (p > 0.05). Accordingly, Two-way ANOVA outcome showed that the 'type of restoration' or 'test time' had statistically significant effect on the AFM test (p < 0.05). Regarding Fluoride specific ion electrode test 2-way ANOVA followed by Least Significant Difference (LSD) Post-hoc test revealed significant difference among the groups (p < 0.05). It showed that SDI GIC group after 14 days of measurement had the highest mean of fluoride release (36.38 ± 3.16 PPM) and SDI RMGIC after 30 days of measurement had the second highest mean of fluoride release (43.28 ± 1.89 PPM). Finally, regarding the micromorphological analysis using SEM, a slight difference was observed between the studied groups. CONCLUSIONS: Based on the results of this study, various coatings enhance surface roughness in the initial 24 h of restoration insertion. Different coat types seems that have no influence on fluoride release and the micromorphological features of the restoration/dentin interface.

Performance evaluation of carbon quantum dots impregnated glass ionomer cement to avoid peri-implant disease.

Dental cement residues exacerbate peri-implant tissue irritation and peri-implantitis. The present study aims to evaluate the cytotoxicity, physiochemical, optical, and rheological properties of carbon quantum dots (CQDs) impregnated glass ionomer cement (GIC). Surface passivated fluorescent CQDs were synthesized using citric acid via thermal decomposition and blended with GIC. Characterization studies and rheological measurements were made to evaluate their performance. 3D-printed dental implant models cemented with GIC and GIC-CQD were compared to analyze excess cement residues. MTT assay was performed with human dental pulp stem cells (hDPSCs) and statistically analyzed using ANOVA and Tukey's test. CQDs with a particle dimension of ∼2 nm were synthesized. The amorphous property of GIC-CQD was confirmed through XRD. The fluorescence properties of GIC-CQD showed three times higher emission intensity than conventional GIC. GIC-CQD attained maturation with a setting time extended by 64 s than GIC. Cement residue of size 2 mm was detected with a UV light excitation at a distance between 5 to 10 cm. Biocompatibility at 0.125 mg ml-1dilution concentrations of GIC-CQD showed viability greater than 80% to hDPSCs. For the first time, we report that CQDs-impregnated GIC is a unique and cost-effective strategy for in-situ detection of excess cement rapidly using a hand-held device. A novel in-situ rapid detection method enables the dentist to identify residual cement of size less than 2 mm during the implantation. Therefore, GIC-CQD would replace conventional GIC and help in the prevention of peri-implant diseases.

Comparative Evaluation of Shear Bond Strength of Resin-modified Glass Ionomer Cement with ProRoot MTA and MTA Angelus.

AIM: The aim of the present study was to evaluate the shear bond strength of resin-modified glass ionomer cement with two different types of mineral trioxide aggregate at different time intervals. MATERIALS AND METHODS: A total of 80 cylindrical blocks were prepared using a self-cure acrylic resin with a central cavity of 4 mm internal diameter and 2 mm height. The prepared samples were randomly divided into two groups (n = 40 each) according to the type of MTA cements used (ProRoot MTA and MTA Angelus). Two groups were further sub-divided into four sub-groups of 10 samples each according to the different time intervals. ProRoot MTA and MTA Angelus were placed in the prepared cavity and a wet cotton pellet was placed over the filled cavity. A hollow plastic tube was placed over the MTA surface and resin-modified glass ionomer cement (RMGIC) was placed into the hollow plastic tube and light-cured (Spectrum 800, Dentsply Caulk Milford, DE, USA) according to the time intervals decided. After light curing the plastic tubes were removed carefully and the specimens were stored at 37°C and 100% humidity for 24 hours to encourage setting of MTA. The specimens were mounted in a universal testing machine (ADMET) and a crosshead speed of 0.5 mm/min was applied to each specimen by using a knife-edge blade until the bond between the MTA and RMGIC failed. The data were statistically analyzed using ANOVA, post hoc Tukey's t-test and Fisher's t-test and p-value ≤ 0.5 was considered significant. RESULTS: For both ProRoot MTA and MTA Angelus there was no statistically significant difference between 45 minutes and 24 hours (p-value ≥ 0.8). For ProRoot MTA, shear bond strength value at 10 minutes were significantly lower than 45 minutes and 24 hours group. However, for MTA Angelus, shear bond strength value at 10 minute was not significantly different from 45 minutes group (p-value ≥ 0.3). For both ProRoot MTA and MTA Angelus shear bond strength value at 0 minute were the least and were significantly lower than 10 minutes, 45 minutes, and 24 hours, respectively (p-value ≥ 0.000). CONCLUSION: Resin-modified glass ionomer cement can be layered over MTA Angelus after it is allowed to set for 10 minutes. However, ProRoot MTA should be allowed to set for at least 45 minutes before the placement of RMGIC to achieve better shear bond strength. CLINICAL SIGNIFICANCE: Due to the variety of types of mineral trioxide aggregate cements available in dentistry, it is justifiable to emphasize on different time intervals as it may affect the shear bond strength of restorative cements. Such information is pivotal for the clinicians while using mineral aggregate-based cements that receive forces from the condensation of restorative materials or occlusion, as the compressive strength may be affected due to different time intervals. How to cite this article: Tyagi N, Chaman C, Anand S, et al. Comparative Evaluation of Shear Bond Strength of Resin-modified Glass Ionomer Cement with ProRoot MTA and MTA Angelus. J Contemp Dent Pract 2024;25(1):35-40.

Adhesion of glass ionomer cements to primary dentin using a universal adhesive.

BACKGROUND: Glass ionomers are widely used for restoring carious primary teeth. However, their ability to bond to primary dentin is considered a challenge in pediatric dentistry. OBJECTIVES: The study aimed to evaluate the microshear bond strength (µSBS) of a resin-modified glass ionomer (RMGI) and a high-viscosity glass ionomer cement (Hv-GIC) to primary dentin using a universal adhesive. MATERIAL AND METHODS: Thirty human primary maxillary canines were cut in half and prepared for the µSBS test. The specimens (N = 60) were assigned to 6 groups. Three groups were defined for RMGI (FUJI II LC) and 3 groups for Hv-GIC (EQUIA Forte): with an immediately curing adhesive (G-Premio); with a delayed curing adhesive; and without an adhesive (control group). After preparing the dentin surfaces, the glass ionomers were bonded using Tygon® tubes with an internal diameter of 0.7 mm. The µSBS test was performed, and the data was analyzed using two-way analysis of variance (ANOVA) followed by Tukey's post hoc test. Additionally, the failure modes were determined using a stereomicroscope. Six specimens, one for each study group, were prepared for scanning electron microscopy (SEM) analysis to observe the glass ionomer-dentin interface. RESULTS: The type of glass ionomer did not have a significant effect on the µSBS (p = 0.305). Groups that received universal adhesive application prior to glass ionomer exhibited a significantly higher µSBS (p < 0.0001). However, there was no significant difference between the immediately curing and delayed curing groups (p = 0.157). The predominant failure mode was mixed failure. CONCLUSIONS: Higher bond strength of glass ionomers to primary teeth can be achieved by using universal adhesives, which, in addition to the proven benefits of glass ionomers, can improve their clinical success.

Enhanced remineralisation ability and antibacterial properties of sol-gel glass ionomer cement modified by fluoride containing strontium-based bioactive glass or strontium-containing fluorapatite.

OBJECTIVES: This study aimed to compare two types of bioactive additives which were strontium-containing fluorinated bioactive glass (SrBGF) or strontium-containing fluorapatite (SrFA) added to sol-gel derived glass ionomer cement (SGIC). The objective was to develop antibacterial and mineralisation properties, using bioactive additives, to minimize the occurrence of caries lesions in caries disease. METHODS: Synthesized SrBGF and SrFA nanoparticles were added to SGIC at 1 wt% concentration to improve antibacterial properties against S. mutans, promote remineralisation, and hASCs and hDPSCs viability. Surface roughness and ion-releasing behavior were also evaluated to clarify the effect on the materials. Antibacterial activity was measured via agar disc diffusion and bacterial adhesion. Remineralisation ability was assessed by applying the material to demineralised teeth and subjecting them to a 14-day pH cycle, followed by microCT and SEM-EDS analysis. RESULTS: The addition of SrFA into SGIC significantly improved its antibacterial property. SGIC modified with either SrBGF or SrFA additives could similarly induce apatite crystal precipitation onto demineralised dentin and increase dentin density, indicating its ability to remineralise dentin. Moreover, this study also showed that SGIC modified with SrBGF or SrFA additives had promising results on the in vitro cytotoxicity of hASC and hDPSC. SIGNIFICANT: SrFA has superior antibacterial property as compared to SrBGF while demonstrating equal remineralisation ability. Furthermore, the modified SGIC showed promising results in reducing the cytotoxicity of hASCs and hDPSCs, indicating its potential for managing caries.

A comparative evaluation of fluoride release and rechargeability in conventional GIC (type II), pediatric GIC (type IX), and Cention-N: an in vitro study.

PURPOSE: A comparative evaluation of fluoride release and re-chargeability in conventional glass ionomer cement (GIC) (type II), Pediatric GIC (type IX), and Cention-N-an in vitro study at an interval of first, fourteenth, and twenty first days. METHODS: Three groups of test materials, each with twenty samples, were prepared. Measurements of the cumulative fluoride release [parts per million (ppm)] and re-release measured on the first, fourteenth, and twenty first days. Analysis of variance (ANOVA) was used to compare the means for different readings, and Tukey's post hoc analysis was used to compare each group with each other. RESULTS: Initial and subsequent fluoride release of Cention-N at days one, fourteen, and twenty-one were all noticeably higher than those of conventional and pediatric GIC. CONCLUSION: Compared to the Conventional and Pediatric GIC restorative materials, Cention-N was more effective in the initial and fluoride re-release.

Changes in enamel hardness, wear resistance, surface texture, and surface crystal structure with glass ionomer cement containing BioUnion fillers.

This study investigated the potential of BioUnion filler containing glass ionomer cement (GIC) to enhance the properties of enamel surrounding restorations, with a specific focus on the effect on hardness. The hardness of the bovine enamel immersed in the cement was measured using Vickers hardness numbers. Following sliding and impact wear simulations, the enamel facets were examined using confocal-laser-scanning microscopy and scanning-electron microscopy. Surface properties were further analyzed using energy-dispersive X-ray spectroscopy and X-ray diffraction (XRD). A significant increase in Vickers hardness numbers was observed in the BioUnion filler GIC after 2 days. Furthermore, the mean depth of enamel facets treated with BioUnion filler GIC was significantly less than that of untreated facets. Characteristic XRD peaks indicating the presence of hydroxyapatite were also observed. Our findings imply that GIC with BioUnion fillers enhances the mechanical properties of the tooth surface adjacent to the cement.

Assessing the impact of dental restorative materials on fibroblast cells: an immunohistochemical and ELISA analysis.

In this study, our aim was to investigate the effects of restorative materials such as composite, compomer and high viscosity glass ionomer, which are frequently used in dentistry, on L929 fibroblast cells by evaluating the oxidative stress parameters, pro- and anti-inflammatory cytokines, and apoptosis markers. L929 fibroblast cells were cultured, and dental filling materials were applied in two doses (50 and 100 µl). Immunohistochemical staining was performed for experimental groups with Anti-Bax and Anti-Caspase 9 antibodies. Then, ELISA technique was used to detect the level of TNF-alpha, TGF-beta, IL-1-beta, IL-6, IL-10, LPO and CAT. In the light of the data, the examined dental filling materials were effective on increasing the TGF-beta, IL-10, LPO and CAT levels, and decreasing the TNF-alpha, IL-1-beta, and IL-6 levels. The histological micrographs were also support the issues. When the levels of H-score in Caspase 9 labeled micrographs were evaluated, the mean of the control group was lower than the mean of the experimental groups. Biocompatibility varies according to the content of the material, the amount of residual monomer, and its solubility. Although all the experimental groups have cytotoxic effects, the least effect is seen in the Omnichroma group.

In vitro remineralization by various ion-releasing materials of artificially demineralized dentin: A micro-CT study.

OBJECTIVE: The aim of this study was to evaluate the remineralizing properties of ion-releasing restorative materials on pH cycling-induced carious dentin. METHODS: Fifty sound molars were freshly extracted. The occlusal surfaces were abraded using water-cooled sandpaper (800 grit). The residual crowns were embedded in self-cured acrylic resin with the flat dentin surface exposed. A mesio-distal trench was created using a calibrated 0.5 mm deep occlusal reduction burr, and artificial dentin caries were generated by pH cycling. Then, teeth were randomly assigned to five groups according to the ion-releasing material used. For each sample, micro-CT acquisitions were performed at various intervals. Remineralization was assessed by mean gray value (MGV) measurements after registration and segmentation of the region of interest with 3D Slicer software. One-way repeated-measures ANOVA followed by Tukey's post hoc test was used to investigate the difference in MGVs among the various groups. RESULTS: Only Cention Forte showed significantly increased MGVs after 4 weeks compared to demineralized dentin. MGVs were higher, but not significantly, after placement of the restorative materials, including in the resin composite control group. These results can be explained by the radiopacity of the materials. SIGNIFICANCE: Cention Forte, the material with the highest radiopacity, showed a significant increase in the MGVs of artificially carious dentin after 4 weeks. However, the study of dentin remineralization by micro-CT could be impacted by the radiopacity of the restorative materials used. The relevance of this examination for the study of dentinal remineralization should be investigated.

In vitro characterization of a novel resin-based restorative material containing alkaline fillers.

OBJECTIVE: In this study, a comparative evaluation of the physicochemical properties of Cention N and other direct restorative materials was performed. Three restorative materials-a resin-modified glass ionomer (Fuji II LC), an alkasite-based resinous material (Cention N), and a resin composite (Tetric N Ceram)-were characterized in terms of degree of conversion, Knoop hardness number (KHN) ratio, flexural strength, elastic modulus, water sorption, water solubility, microshear bond strength to dentin, immediate microleakage, and radiopacity. METHODOLOGY: The microshear bond strength to dentin and microleakage of Cention N were evaluated with and without the application of an adhesive system (Tetric N Bond Universal). A one-way ANOVA test was used to analyze the data in terms of degree of conversion, KHN ratio, water sorption, water solubility, microshear bond strength to dentin, and radiopacity. A two-way ANOVA test (carried out considering the material type and ethanol aging as factors) was used to analyze the data in terms of flexural strength and elastic modulus. The Kruskal-Wallis test was used to statistically analyze the data on microleakage. A significance level of α=0.05 was used for all tests. RESULTS: Fuji II LC was found to have the highest degree of conversion, water sorption, and microleakage, as well as the lowest flexural strength. Cention N had the highest solubility; when used with an adhesive system, it achieved bond strength and microleakage similar to those of the Tetric N Ceram composite. Tetric N Ceram had the highest degree of conversion, KHN ratio, and radiopacity. Conclusion: The properties of Cention N validate its efficacy as an alternative direct restorative material when used in conjunction with an adhesive system.

Effect of a calcium silicate cement and experimental glass ionomer cements containing calcium orthophosphate particles on demineralized dentin.

OBJECTIVE: The study aims to evaluate the effect of a glass ionomer cement (GIC; Fuji 9 Gold Label, GC) with added calcium orthophosphate particles and a calcium silicate cement (CSC; Biodentine, Septodont) regarding ion release, degradation in water, mineral content, and mechanical properties of demineralized dentin samples. METHODS: GIC, GIC + 5% DCPD (dicalcium phosphate dihydrate), GIC + 15% DCPD, GIC + 5% ß-TCP (tricalcium phosphate), GIC + 15% ß-TCP (by mass), and CSC were evaluated for Ca2+/Sr2+/F- release in water for 56 days. Cement mass loss was evaluated after 7-day immersion in water. Partially demineralized dentin disks were kept in contact with materials while immersed in simulated body fluid (SBF) at 37 °C for 56 days. The "mineral-to-matrix ratio" (MMR) was determined by ATR-FTIR spectroscopy. Dentin hardness and elastic modulus were obtained by nanoindentation. Samples were observed under scanning and transmission electron microscopy. Data were analyzed by ANOVA/Tukey test (α = 0.05). RESULTS: Ca2+ release from CSC and GIC (µg/cm2) were 4737.0 ± 735.9 and 13.6 ± 1.6, respectively. In relation to the unmodified GIC, the addition of DCPD or ß-TCP increased ion release (p < 0.001). Only the dentin disks in contact with CSC presented higher MMR (p < 0.05) and mechanical properties than those restored with a resin composite used as control (p < 0.05). Mass loss was similar for GIC and CSC; however, the addition of DCPD or ß-TCP increased GIC degradation (p < 0.05). CONCLUSION: Despite the increase in ion release, the additional Ca2+ sources did not impart remineralizing capability to GIC. Both unmodified GIC and CSC showed similar degradation in water. CLINICAL RELEVANCE: CSC was able to promote dentin remineralization.

Bioactivity and remineralization potential of modified glass ionomer cement: A systematic review of the impact of calcium and phosphate ion release.

This systematic review investigates the effectiveness of calcium and phosphate ions release on the bioactivity and remineralization potential of glass ionomer cement (GIC). Electronic databases, including PubMed-MEDLINE, Scopus, and Web of Science, were systematically searched according to PRISMA guidelines. This review was registered in the PROSPERO database. Five eligible studies on modifying GIC with calcium and phosphate ions were included. The risk of bias was assessed using the RoBDEMAT tool. The incorporation of these ions into GIC enhanced its bioactivity and remineralization properties. It promoted hydroxyapatite formation, which is crucial for remineralization, increased pH and inhibited cariogenic bacteria growth. This finding has implications for the development of more effective dental materials. This can contribute to improved oral health outcomes and the management of dental caries, addressing a prevalent and costly oral health issue. Nevertheless, comprehensive longitudinal investigations are needed to evaluate the clinical efficacy of this GIC's modification.

Shear bond strength of calcium silicate-based cements to glass ionomers.

BACKGROUND: A shear bond strength between the biomaterial and restorative material is crucial for minimizing bacterial microleakage and ensuring a favorable long-term prognosis for vital pulp therapy. This study aimed to conduct a comparative evaluation of the shear bond strength between calcium silicate-based biomaterials utilized in vital pulp treatment and various glass ionomer cement materials, both with and without the application of adhesive agents. METHODS: A total of 270 acrylic blocks, each featuring cavities measuring 4 mm in diameter and 2 mm in depth, were prepared. Calcium silicate-containing biomaterials (ProRoot MTA, Medcem Pure Portland Cement, and Medcem MTA), following manufacturers' instructions, were placed within the voids in the acrylic blocks and allowed to set for the recommended durations. The biomaterial samples were randomly categorized into three groups based on the restorative material to be applied: conventional glass ionomer cement, resin-modified glass ionomer cement, and bioactive restorative material. Using cylindrical molds with a diameter of 3.2 mm and a height of 3 mm, restorative materials were applied to the biomaterials in two different methods, contingent on whether adhesive was administered. After all samples were incubated in an oven at 37 °C for 24 h, shear bond strength values were measured utilizing a universal testing device. The obtained data were statistically evaluated using ANOVA and post-hoc Tukey tests. RESULTS: The highest shear bond strength value was noted in the Medcem MTA + ACTIVA bioactive restorative material group with adhesive application, while the lowest shear bond strength value was observed in the ProRoot MTA White + Equia Forte HT Fil group without adhesive application (P < 0.05). CONCLUSION: Activa Bioactive Restorative may be considered a suitable restorative material in combination with calcium silicate-based biomaterials for vital pulp treatment. The application of adhesives to calcium silicate-based biomaterials can effectively address the technical limitations.

Delayed vs. immediate placement of restorative materials over Biodentine and RetroMTA: a micro-shear bond strength study.

BACKGROUND: The aim of the present study was to investigate the micro-shear bond strength (µSBS) of various restorative materials applied on two different fast-setting calcium silicate-based materials and to evaluate the effect of restoration time on µSBS. METHODS: A total of 180 acrylic blocks with a cavity in the center were randomly divided into 2 main groups according to the capping material to be used (Biodentine or RetroMTA). The specimens were also randomly divided into 3 groups according to the restoration time (3 min, 12 min, 24 h). After the specified waiting periods, glass hybrid material (EQUIA Forte HT), resin composite (Filtek Z550) and light-cured calcium silicate material (Theracal LC) were placed on the specimens with tygon tubes. The specimens were kept for 24 h and then subjected to µSBS test. Statistical analysis was performed by 3-way ANOVA followed by Tukey test for pairwise comparisons (α = 0.05). RESULTS: There is a statistically significant difference (p < 0.05) between the µSBS values obtained by applying resin composite on RetroMTA after different setting times (24 h > 12 min > 3 min). The µSBS obtained for the Biodentine-resin composite at the end of the 3 min setting time is significantly lower (p < 0.05) than the µSBS values at 12 min and 24 h. For both calcium silicate cements, at the end of all time periods, the µSBS obtained when resin composite was applied at the end was higher than the other materials (p < 0.05). CONCLUSIONS: For Biodentine-resin composite bonding, the manufacturer's recommendation of 12 min can be considered an appropriate time, whereas for RetroMTA-resin composite bonding, the µSBS increased as the waiting time increased. Regardless of the waiting time, it is recommended to prefer direct composite resin restoration over Biodentine and RetroMTA.

Effect of bioactive glass particles on mechanical and adhesion properties of resin cements.

PURPOSE: The aim of this study is to evaluate the mechanical and adhesive properties of three different resin cements with bioactive glass (BAG) incorporated in two different ratios. METHODS: BAG was added to different resin cements (3M Rely-X Ultimate, GC Link Ace, and GC Link Force) in different ratios (5% and 10% by weight). The three-point flexural strength, microhardness, and bond strength properties were evaluated. The fracture types of the groups were then analyzed using a stereo microscope. The data were analyzed using a multifactorial analysis of variance and Tukey's post-hoc tests (α < 0.05). RESULTS: The addition of BAG reduced the flexural strength of the resin cements (P < 0.05).The effect of BAG addition on the Vickers microhardness value was significantly different for each cement group (P < 0.05). In addition, with the exception of the GC link force group (10% BAG addition), the BAG addition decreased the bond strength of cements to dentin in all the groups (P = 0.171). CONCLUSIONS: The results of this study confirmed that different resin cements comprising different ratios of BAG exhibited different flexural strength, hardness, and bond-strength properties. Since the bond strength values increased with the addition of 10% BAG in the GC Link Force cement group, the effects of different BAG compositions could be worth investigating in future studies.

Influence of surface pre-reacted glass-ionomer (S-PRG) filler eluate on collagen morphology, remineralization, and ultimate tensile strength of demineralized dentin.

OBJECTIVE: To evaluate the effect of ions released from surface pre-reacted glass-ionomer (S-PRG) filler on collagen morphology, remineralization, and ultimate tensile strength (UTS) of demineralized dentin. MATERIALS AND METHODS: Bovine incisor root dentins were demineralized with EDTA and divided into three treatment groups: 1) water (control); 2) S-PRG filler eluate; 3) 125 ppm sodium fluoride (NaF). After a 3-min treatment, the specimens were stored in simulated body fluid (SBF) for 3 months. Collagen morphology and remineralization were assessed using transmission electron microscopy (TEM), scanning electron microscopy (SEM), and Fourier-transform infrared spectroscopy (FTIR). Additionally, ultimate tensile strength (UTS) was measured. RESULTS: TEM and SEM demonstrated that S-PRG induced more effective remineralization compared to NaF, while the control group exhibited faint mineral deposition with collagen degradation. S-PRG displayed the most homogenous mineral deposition in collagen fibrils, along with closure of interfibrillar spaces. Extensive mineral precipitation was observed within dentinal tubules in the S-PRG group. In addition, S-PRG filler eluate demonstrated significantly higher phosphate-to-amide ratio and UTS compared to NaF and control groups (p < 0.05). CONCLUSIONS: Ion released from S-PRG filler positively influenced collagen morphology, remineralization, and ultimate tensile strength of demineralized dentin. CLINICAL SIGNIFICANCE: S-PRG filler enhances remineralization and improve the biomechanics of demineralized dentin.

Hydroxyapatite-based dental inserts: Microstructure, mechanical properties, bonding efficiency and fracture resistance of molars with occlusal restorations.

This study aimed to (1) comparatively analyze properties of Sr- and Mg-substituted hydroxyapatite (HAP)-based dental inserts; (2) evaluate insert bonding to restorative materials, and (3) evaluate the effect of doped HAP inserts on fracture resistance (FR) of human molars with large occlusal restorations. By ion-doping with Sr or Mg, 3 insert types were obtained and characterized using XRD, SEM, Vickers hardness and fracture toughness. Shear bond strength (SBS) was determined between acid etched or unetched inserts and following materials: Maxcem cement (Kerr); Filtek Z250 (3M) bonded with Single Bond Universal (SBU; 3M) or Clearfil Universal (Cf; Kuraray). Modified Class I cavities were prepared in 16 intact molars and restored using insert + composite or composite only (control) (n = 8/group). FR of restored molars was determined by static load until fracture upon thermal cycling. Fracture toughness was similar between Sr/Mg-doped inserts (0.94-1.04 MPam-1/2 p = .429). Mg-doped inserts showed greater hardness (range 4.78-5.15 GPa) than Sr6 inserts (3.74 ± 0.31 GPa; p < .05). SBS for SBU and Cf adhesives (range 7.19-15.93 MPa) was higher than for Maxcem (range 3.07-5.95 MPa) (p < .05). There was no significant difference in FR between molars restored with insert-containing and control restorations (3.00 ± 0.30 kN and 3.22 ± 0.42 kN, respectively; p > .05). HAP-based inserts doped with Mg/Sr had different composition and mechanical properties. Adhesive bonding to inserts resulted in greater bond strength than cementation, which may be improved by insert acid-etching. Ion-doped HAP inserts did not affect FR of restored molars. In conclusion, HAP-based dental inserts may potentially replace dentin in large cavities, without affecting fracture resistance of restored teeth.

Glass ionomer cement with calcium-releasing particles: Effect on dentin mineral content and mechanical properties.

OBJECTIVE: to evaluate the effect a glass ionomer cement (GIC) containing hydroxyapatite (HAp) or calcium silicate (CaSi) particles on mineral content and mechanical properties of demineralized dentin. Ion release and compressive strength (CS) of the cements were also evaluated. METHODS: GIC (Fuji 9 Gold Label, GC), GIC+ 5%HAp and GIC+ 5%CaSi (by mass) were evaluated. Ion release was determined by induced coupled plasma optical emission spectroscopy (Ca2+/Sr2+) or ion-specific electrode (F-) (n = 3). A composite (Filtek Z250, 3 M ESPE) was used as control in remineralization tests. Demineralized dentin discs were kept in contact with materials in simulated body fluid (SBF) at 37 °C for eight weeks. Mineral:matrix ratio (MMR) was determined by ATR-FTIR spectroscopy (n = 5). Dentin hardness (H) and elastic modulus (E) were determined by nanoindentation (n = 10). CS was tested after 24 h and 7d in deionized water (n = 12). Data were analyzed by ANOVA/Tukey test (α = 0.05). RESULTS: Ca2+ and Sr2+ release was higher for the modified materials (p < 0.05). Only GIC+ 5%HAp showed higher F- release than the control (p < 0.05). All groups showed statistically significant increases in MMR, with no differences among them after 8 weeks (p > 0.05). No differences in dentin H or E were observed among groups (p > 0.05). HAp-modified GIC showed increased initial CS, while adding CaSi had the opposite effect (p < 0.05). After 7 days, GIC+ 5%CaSi presented lower CS in relation to control and GIC+ 5%HAp (p < 0.05). SIGNIFICANCE: GIC modification with HAp or CaSi affected CS and increased ion release; however, none of the groups showed evidence of dentin remineralization in comparison to the negative control.